物性指标
均标注测试标准与条件
- Hardness
- 90 Shore A (ASTM D2240)
- Tensile strength
- 15.5 MPa (ASTM D412)
- Elongation at break
- 149 % (ASTM D412)
- Compression set
- 16 % (ASTM D395 Method B, 70 h @ 200 °C, 25 % deflection, Type B)
- Service temperature
- -10 °C to +290 °C
- Process compatibility
- Dry + Wet
- Seal type
- Static + Dynamic
- Colour
- Black
压缩永久变形必须结合测试条件阅读 — 300 °C 下测得的 23 % 无法说明 200 °C 下的表现。本站每个数值均标注其测试温度与时长，以便在同口径下比较不同牌号。
典型应用
High-pressure gas, wellhead / BOP and extrusion-critical service
可比牌号
对照
| 牌号 | 硬度 | 使用温度 | 压缩永久变形 | 对照依据 |
|---|---|---|---|---|
| Kalrez® 7090 | 90 Shore A | −26 to +325 °C | — | Matching durometer for high-pressure gas service; their upper limit is higher. |
| Kalrez® 0090 | 95 Shore A | −27 to +250 °C | — | Slightly higher durometer, commonly specified for rapid gas decompression duty. |
| Chemraz® 510 | 90 Shore A | −30 to +230 °C | — | Matching durometer; lower upper temperature limit. |
仅为参数级对照 — 上述对照依据各牌号公开发布的硬度、温度与压缩永久变形数据整理，仅供初步筛选，不构成等效性声明。实际密封表现取决于您的介质、温度、压力、运动方式与沟槽设计。更换已认证零件前请以样品验证。